Dental MILLING DISCS

ZIRCONIA DISCS DIGITECH are designed to provide the best results in your restorations. 

Made with the best ZIRCONIA powder providing excellent performance and MILLING precision. 

Offered in all platforms 98.5mm 98mm 95mm 71mm and Cerec compatible. 

ALL our DIGITECH ZIRCONIA MILLING DISCS 

are manufactured with :

* First grade ZIRCONIA powder
* Shrinkage adjusted for 20%
DIGITECH ZIRCONIA DISCS counts with the following types of material : 

4D ST Multilayer
ST Multilayer 
ST Super translucent 
TT  Anterior Translucency 
HS High Strength 

Characteristics DIGITECH ZIRCONIA MILLING DISCS

DIGITECH 4D disc, is a 5 layers dental multilayer zirconium oxide  with gradient translucency, color and high translucency. 

DIGITECH 4D Functional  MULTILAYER 1300 mpa   46% Translucency 

layer 1    1027 mpa    46.6% translucency
layer 2     1105  mpa   45.6% translucency
layer 3     1205 mpa    44.3% translucency
layer 4     1300 mpa    43.0% translucency
layer 5     1300 mpa    43.0% translucency

Also Available as

DIGITECH 4D Anterior AT MULTILAYER 1030 mpa    48.5% Translucency 

Advantages of 4D Multilayer ZIRCONIA DISCS:

Natural color gradient
Translucency gradient with special adjustment
16 Vita shades + 4 bleach shades

DIGITECH HS Mono white 

The DIGITECH High Strength ZIRCONIA blanks used for monolithic or anatomically reduced anterior restorations and framework bridge combined with porcelain. 

With high strength (more than 1400Mpa) and good translucent(39%) it offers to the labs with its high strength and good translucent.

DIGITECH ST Super Translucent ( mono and Multilayer ) 

DIGITECH Super translucent Multilayer disc is super high translucent ZIRCONIA with integrated shade and translucency of 5 layers gradient. Natural color and translucent gradient simulate tooth enamel, dentine and cervical shades. Simply operation for dental technician without staining.

Advantage

• Super strength more than 1100Mpa and super translucent more than 43%
• Available for 16 shades
• Natural simulate teeth after sintering 
• Fully anatomical crowns and multi-unite bridges

DIGITECH TT Anterior Translucency 

DIGITECH Anterior Top translucent with ultra translucent previously only known in lithium disilicate. With 49% transmits and more than 600 PMA, It is best choice for anterior , posterior restoration, veneer, onlay, inlay and high esthetic restoration up to 3 unite bridge.

Advantage

Ultra translucent ZIRCONIA for highly esthetic anterior and posterior regions

FIRING CHART DIGITECH ZIRCONIA MILLING DISCS

* Starting temperature: Room Temperature

* Temperature Heating rate 4 Celcius per minute to 800 degrees Celcius where we hold for 10 minutes 

* Now Sinterization temperature : 

           HS and ST 1530 Celsius 2 hours

           AT / 4D  1450 to 1500 Celcius 2 hours  ( standard 1480 Celcius ) 

* Temperature Cooling Rate 4 Celcius per minute

* Total Cycle time: 16 hours .

Then open door, don't forget to decontaminate your sinter oven once a week, or at least once a month. This advice is for every sinter oven in the market, regardless of brand name, or origin.