CoCr dry mill - easy as wax
Ceramill Sintron revolutionises CNC-based dry processing of non-precious metal restorations using desktop milling machines in-house in the laboratory. The wax-like texture of Ceramill Sintron allows the material to be dry milled effortlessly. During the subsequent SINTERING process under shielding gas atmosphere the frameworks achieve their final material properties – a CoCr unit with very homogeneous material structure. Any conventional CoCr framework porcelain can then be used for veneering. Ceramill Sintron was developed in collaboration with the Fraunhofer IFAM Dresden, Germany.
"The combination of Ceramill Sintron and the Ceramill Argotherm opened up a completely new world to me - guaranteed reliable, precise and perfectly fitting results. The same process as for zirconia, just milling and SINTERING!"
Perio Dental Lab
"Sintron gives us back the control to create exactly what clients need. With this material we have the ability to engineer new solutions in-house, for frameworks that would have otherwise been outsourced."
Adelaide Laboratories
- Crowns & Bridges, anatomically reduced & fully anatomical
- Telescope
- Multi-unit, screw-retained restorations on titanium
- Custom abutments on titanium bases
- Anatomically reduced and fully anatomical crown and bridge frameworks in the anterior and posterior region
- Effortless dry milling and minimum cutter wear thanks to wax-like texture
- Comfortable handling due to easy reworking and finishing of the milled framework in the green state
- Maximum process reliability thanks to homogeneous, distortion-free frameworks
- Excellent strength values, bonding strength and biocompatibility
- Tensile Strength: 900 MPa
- Modulus of Elasticity: 200 GPa
- Density: 7.9 g/cm3
- Vickers Hardness: 270 HV 10
- CTE 25 - 500 °C: 14,5 *10-6/K
- Elongation at rupture: 30 %
- Open porosity: 0 %
- Color: silver
- Oxide color: grey-green
- Proof stress (Rp 0,2%): 450 MPa
- Co: 66
- Cr: 28
- Mo: 5
- Si: < 1
- Fe: < 1
- Mn: <1
- In accordance with DIN EN ISO 22674:2007 the alloy is free of nickel, beryllium, gallium and cadmium