KEYPRINT - KeyCast, 1kg - #4220000 - Highly precise resin for investment molding. Burns out with no residue. 3dResin

KEYPRINT  - KeyCast, 1kg - #4220000 - Highly precise resin for investment molding. Burns out with no residue.  3dResin
KEYPRINT  - KeyCast, 1kg - #4220000 - Highly precise resin for investment molding. Burns out with no residue.  3dResin KEYPRINT  - KeyCast, 1kg - #4220000 - Highly precise resin for investment molding. Burns out with no residue.  3dResin
SKU: 470559 - IN STOCK
$250.00
$229.16
You save: $20.84 (8%)
Quantity:

Minimum quantity is 1.

Manufacturer #
4220000
Manufacturer
Model
KeyPRINT
Sizes
1Kg
Features
WAX Casting
Package
1pk
Only 2 Left - Order soon!

Earn up to 241 rewards points with this product!

Join today and start earning rewards points and unlock exclusive savings with US Dental Depot's Customer Loyalty Rewards Program

SmileRewards Club

Description

Accurate
Low Shrinkage
High Speed
KeyCAST®
Highly precise resin for investment molding.
Burns out with no residue.
•   #4220000 KeyCAST (1kg)
•   #4200000 KeyCAST (0.5kg)
USES AND ADVANTAGES
KeyCAST is compatible with rapid burnout and gradual temperature ramp workflows, with no residual ash.
⦿  KeyCAST is used with chrome, cobalt, gold, and silver
⦿  Low shrinkage formula controls thermal expansion to yield pore-free and accurate castings
Casting PROCEDURE AND RECOMMENDATIONS
For best results KEYSTONE recommends using Kerr “Satin Cast 20” or Ransom & Randolph “Ultra-Vest” investment material. This will ensure no adverse reactions between the casted part and investment material during the burnout process.
For best results, flasks should be vacuum or centrifuged to remove any air bubbles. Flasks should be bench cured for 2 hours prior to burnout.
KEYSTONE recommends customers to allow >4mm of space between part edges and the outside edge of flask. This will ensure proper absorption of expansion during burnout.
Note: It is extremely important to hold the temperature ramp at 500°F (260°C) for at least one hour, depending on the flask size. This will ensure proper part dimensional stability.
TECNICAL DATA
PROPERTY
Flexural Strength (MPa)
Flexural Modulus (MPa)
Tensile Strength
Young's Modulus (MPa)
Elongation at Break %
CTE 0-150˚C (32-302˚F)
CTE 150-250˚C (302-482˚F)
CTE >250˚C (>482˚F)
Shrinkage
Burnout
PROCEDURE
ASTM D790
ASTM D790
ASTM D638
ASTM D638
ASTM D638
ASTM E831
ASTM E831
ASTM E831
ASTM D792
KEY'CAST
15
340
9.1
220
16%
168 x 10-6m/(m.˚C)
64 x 10-6m/(m.˚C)
<0m/(m.˚C)
<2%
<0.05%
TECNICAL DOCUMENTS
SDS
SELL SHEET
PRINTER SETTINGS

Related Products